High-temperature Young's moduli and dilatation behavior of silica refractories. Issue 1 (January 2016)

• Record Type: Journal Article
• Authors: Pabst, Willi; Gregorová, Eva; Kloužek, Jaroslav; Kloužková, Alexandra; Zemenová, Petra; Kohoutková, Martina; Sedlářová, Ivona; Lang, Karel; Kotouček, Miroslav; Nevřivová, Lenka; Všianský, Dalibor
• Is Part Of: Journal of the European Ceramic Society. Volume 36:Issue 1(2016)
• Page Start: 209
• Page End: 220
• Publication Date: 2016-01
• Subjects: Silica refractories -- Young's modulus -- Elastic modulus -- Dilatation -- Dilatometry -- Impulse excitation -- Cristobalite -- Tridymite; Ceramic materials -- Periodicals; Composite materials -- Periodicals; Matériaux céramiques -- Périodiques; Composites -- Périodiques; Ceramic materials; Composite materials; Periodicals; Electronic journals; 666.05
• DOI: 10.1016/j.jeurceramsoc.2015.09.020
• Languages: English
• ISSNs: 0955-2219

Abstract

Abstract: Silica refractories with cristobalite–tridymite ratios between 0.83–0.86 and 1.43–1.47 and porosities of 13–17% are characterized by impulse excitation up to 1200 °C and by dilatometry up to 1300 °C. During heating, Young's moduli start to decrease from their room temperature values (9–12 GPa) to about 5–7 GPa at 200 °C, followed by a very steep increase at around 230 °C to values higher than the room temperature values and a nonlinear increase to their final high-temperature values. During cooling, Young's moduli increase even further, exhibit a maximum and a nonlinear decrease that does not follow the heating curve, a very steep decrease at around 200 °C and a final increase to the intial room temperature values, so that a closed loop results during thermal cycling. Dilatometric measurements confirm that the strong increase of the Young's modulus at around 230 °C (during heating) can be attributed to the phase transition between low- and high-temperature cristobalite, while the more gentle—but still very significant—changes in Young's moduli below 200 °C are due to the more diffuse transitions between tridymite subpolymorphs. Microcracks are identified as the primary cause of the low Young's moduli and their increase with temperature.