Processing of 8YSZ and CGO thin film electrolyte layers for intermediate- and low-temperature SOFCs. Issue 5 (May 2015)

• Record Type: Journal Article
• Authors: Van Gestel, Tim; Sebold, Doris; Buchkremer, Hans Peter
• Is Part Of: Journal of the European Ceramic Society. Volume 35:Issue 5(2015:May)
• Page Start: 1505
• Page End: 1515
• Publication Date: 2015-05
• Subjects: Thin-film electrolyte -- 8YSZ -- CGO -- IT-SOFC -- LT-SOFC; Ceramic materials -- Periodicals; Composite materials -- Periodicals; Matériaux céramiques -- Périodiques; Composites -- Périodiques; Ceramic materials; Composite materials; Periodicals; Electronic journals; 666.05
• DOI: 10.1016/j.jeurceramsoc.2014.11.017
• Languages: English
• ISSNs: 0955-2219

Abstract

Abstract: An extensive experimental investigation has been carried out in order to prepare novel thin film electrolytes for enhanced SOFCs. Methods of producing ultra-thin 8 mol% Y2 O3 -doped ZrO2 (8YSZ) electrolytes (<1 μm) and thin 10 mol% Gd2 O3 -doped CeO2 (10CGO) electrolytes (∼1 μm) are presented. The method deposits such thin dense films onto a highly porous anode substrate. As opposed to conventional powder deposition techniques, the method involves depositing a dispersion of nanoparticles to achieve a thin-film mesoporous layer. After sintering at 1400 °C, the deposited mesoporous layer becomes a dense thin film with a thickness of ∼1 μm or even thinner. Such thicknesses are significantly below the limit currently achievable with powder deposition techniques (∼10 μm). The electrolyte layer thickness is comparable to the thicknesses found in micro-SOFCs, but here conventional macroporous SOFC substrates are used. Of considerable importance is the use of a spin-coating process, due to its simplicity and the potential ease of further scaling-up. Results from SEM and leakage tests confirmed that the thin-film electrolytes are homogeneous and have a low number of defects after sintering at 1400 °C. The average leak rate for air was 1–2 × 10 −5 mbar l s −1 cm −2 for the 8YSZ electrolyte and 10 −4 mbar l s −1 cm −2 for the 10CGO electrolyte.