A dense amorphous SiBCN(O) ceramic prepared by simultaneous pyrolysis of organics and inorganics. Issue 4 (March 2016)

• Record Type: Journal Article
• Authors: Tang, Baojun; Zhang, Yue; Hu, Shujuan; Feng, Bo
• Is Part Of: Ceramics international. Volume 42:Issue 4(2016)
• Page Start: 5238
• Page End: 5244
• Publication Date: 2016-03
• Subjects: SiBCN(O) ceramic -- Polycarbosilane -- Amorphous -- Dense -- Pyrolysis; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2015.12.050
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Utilizing active function groups and radicals of polymers (polycarbosilane) to react with a mixture of organics (urea) and inorganics(boric acid) during polymer to ceramic conversion process, a novel SiBCN(O) ceramic was successfully prepared via hot-pressing from 380 to 700 °C combined with following pyrolysis at 1400 °C for 2 h in nitrogen atmosphere. The prepared SiBCN(O) ceramic with a low open porosity of ~4%, which maintained amorphous structure still. Experimental results confirmed that the inorganic network of SiBCN(O) amorphous ceramic was constructed by Si–C, Si–N, Si–O, B–N, and B–O bonds. Pyrolysis product BN served as active filler in densification process of the SiBCN(O) ceramic. Additionally, the introduced oxygen from boric acid could be well controlled and thus effectively improved the densification process of the ceramic.