B-site bismuth doping effect on structural, magnetic and magnetotransport properties of La0.5Ca0.5Mn1−xBixO3. Issue 2 (March 2015)

• Record Type: Journal Article
• Authors: Krichene, A.; Solanki, P.S.; Rayaprol, S.; Ganesan, V.; Boujelben, W.; Kuberkar, D.G.
• Is Part Of: Ceramics international. Volume 42:Issue 2:Part B(2016)
• Page Start: 2637
• Page End: 2647
• Publication Date: 2015-03
• Subjects: Powders: solid state reaction -- Magnetic properties -- Perovskites; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2014.10.163
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: We report the structural, magnetic and magnetotransport properties of polycrystalline La0.5 Ca0.5 Mn1− x Bix O3 ( x =0, 0.02 and 0.05). Refinement of X-ray powder diffraction patterns shows that all samples crystallize with orthorhombic Pnma space group. For x =0.02, the sample shows an increase of unit cell volume as well as Curie temperature TC with the destruction of charge ordering (CO) state existing in parent compound. With 5% bismuth at the B-site, unit cell volume and TC decrease with an enhancement of CO state. Bismuth doping induces a spin glass like state at low temperature with the presence of Griffiths phase above TC . Magnetoresistance (MR) measurements show typical negative colossal magnetoresistance (CMR) at low temperature.