Fatigue performance of a self-piercing rivet joint between aluminum and glass fiber reinforced thermoplastic composite. (February 2016)

• Record Type: Journal Article
• Authors: Gay, Amandine; Lefebvre, Fabien; Bergamo, Sébastien; Valiorgue, Frédéric; Chalandon, Pierre; Michel, Philippe; Bertrand, Philippe
• Is Part Of: International journal of fatigue. Volume 83:Part 2(2016)
• Page Start: 127
• Page End: 134
• Publication Date: 2016-02
• Subjects: Aluminum alloys -- Fiber reinforced material -- Self-piercing joint -- Fatigue strength -- Environmental assisted fatigue; Materials -- Fatigue -- Periodicals; Materials -- Fatigue; Periodicals; 620.1122
• DOI: 10.1016/j.ijfatigue.2015.10.004
• Languages: English
• ISSNs: 0142-1123

Abstract

Highlights: Composite and aluminum sheets are joined by self-piercing riveting and tested under fatigue load. The fatigue joint performances are used to compare two self-piercing rivet shapes. Fatigue tests are carried out under temperature from −40 °C to 90 °C. The SPR joint strength at 2 · 10 6 cycles is equal to more than half of the joint strength in static. Abstract: Lightweight structures are more and more widely used in the automotive industry due to the growing importance of environment regulations related to CO2 emissions. In this context of saving weight, composites offer an alternative to metals because they can achieve a better stiffness to weight ratio. A problematic becomes crucial: which process can be used to join efficiently composite and metallic parts? An innovative way would be the application of self-piercing riveting to thermoplastic composite–metal structure. Since the self-piercing riveting does not require a pre-drilled hole, the time process is short. Nevertheless, this process generates damage in the composite such as fiber cutting and delamination. The aim of this work is to evaluate the fatigue strength of a PA6.6-GF (Glass Fiber reinforced Polyamide 6.6)/Aluminum assembly joined by self-piercing riveting. Experimental results show that the SPR joint achieve high fatigue resistance on uniaxial shearing test. The joint strength at 2 · 10 6 cycles is more than half of the joint strength in static. Joint manufacturing process parameters like the rivet shape were investigated. Some fatigue tests were performed under severe environmental conditions like high temperature. This study shows that process parameters have less influences on the joint strength than the parameters that impact the composite resistance such as the composite type and the test temperature. The composite stresses evolution is useful for the failure modes analyses.