Design of toughened PLA based material for application in structures subjected to severe loading conditions. Part 1. Quasi-static and dynamic tensile tests at ambient temperature. (September 2016)

• Record Type: Journal Article
• Authors: Notta-Cuvier, D.; Bouzouita, A.; Delille, R.; Haugou, G.; Raquez, J.-M.; Lauro, F.; Dubois, P.
• Is Part Of: Polymer testing. Volume 54(2016:Sep.)
• Page Start: 233
• Page End: 243
• Publication Date: 2016-09
• Subjects: Polylactide -- Toughening -- High strain rate behavior -- Industrialization; Polymers -- Testing -- Periodicals; Polymères -- Tests -- Périodiques; 620.1920287
• DOI: 10.1016/j.polymertesting.2016.07.020
• Languages: English
• ISSNs: 0142-9418

Abstract

Abstract: The suitability of a ternary composition 58 wt% polylactide (PLA) - 25 wt% poly(methyl methacrylate) (PMMA) - 17 wt% Impact modifier (Biostrong) for use in technical parts subjected to severe loading conditions was investigated. As a key point, its tensile behavior under high-strain-rate loading, for the moment at ambient temperature, was studied, which has not been done before for any PLA-based composition. Prior to dynamic tensile tests, it was verified that the appealing mechanical properties of PLA-PMMA-Biostrong composition previously achieved with material processed at laboratory scale are kept when the material is produced using industrial extrusion and injection processes. Finally, industrially produced PLA-PMMA-Biostrong composition showed high levels of tensile strength, rigidity and ductility for a wide range of strain-rate and is, therefore, suitable for use in highly-loaded technical parts.