Effect of crystal violet dye on the structural, optical, mechanical and piezoelectric properties of ADP single crystal. (November 2016)

• Record Type: Journal Article
• Authors: Goel, Sahil; Sinha, Nidhi; Yadav, Harsh; Hussain, Abid; Kumar, Binay
• Is Part Of: Materials research bulletin. Volume 83(2016)
• Page Start: 77
• Page End: 87
• Publication Date: 2016-11
• Subjects: A. Optical materials -- B. Crystal growth -- B. Mechanical properties -- B. Piezoelectricity -- C. Raman spectroscopy; Materials -- Periodicals; Crystal growth -- Periodicals; Matériaux -- Périodiques; Cristaux -- Croissance -- Périodiques; Crystal growth; Materials; Periodicals; 620.11
• DOI: 10.1016/j.materresbull.2016.05.023
• Languages: English
• ISSNs: 0025-5408

Abstract

Graphical abstract: Highlights: ⿢ Single crystals of CV dye doped ADP were grown by slow evaporation technique. ⿢ Transmittance, optical window and mechanical strength increased on CV doping. ⿢ Blue emission at 440 nm in PL spectra was partially quenched. ⿢ Transition between load dependent and independent hardness was reported. ⿢ Due to dye doping piezoelectric charge coefficient has been increased. Abstract: Single crystals of pure and crystal violet (CV) dye doped (0.05 mol%) ammonium dihydrogen phosphate (ADP) were grown and characterized. Structural and compositional studies were carried out using XRD, EDAX and FTIR. In UV⿿vis-NIR measurements, characteristic absorption at 590 nm was observed for CV dye, with increased transmittance, wider optical window and increased band gap from 5.80 eV to 6.0 eV. In photoluminescence studies, CV doping resulted in partial quenching of blue emission at 440 nm. The piezoelectric charge coefficient was also enhanced from 1.82 pC/N to 2.78 pC/N. In micro-hardness studies, CV doped crystals exhibited better mechanical strength. The distribution of hardness number was statistically analyzed using Weibull statistics. The values of transition point, critical load, etc. were evaluated for both the crystals. Raman studies revealed that no structural phase transformations were observed after indentation for both the samples.