Application of local mechanical tensioning and laser processing to refine microstructure and modify residual stress state of a multi-pass 304L austenitic steels welds. (April 2015)

• Record Type: Journal Article
• Authors: Sule, Jibrin; Ganguly, Supriyo; Coules, Harry; Pirling, Thilo
• Is Part Of: Journal of manufacturing processes. Volume 18(2015)
• Page Start: 141
• Page End: 150
• Publication Date: 2015-04
• Subjects: Austenitic stainless steel -- Residual stress -- Multi-pass welding -- Microstructure -- Rolling -- Laser processing; Production management -- Data processing -- Periodicals; Manufacturing processes -- Periodicals; Procestechnologie; Productietechniek; Production -- Gestion -- Informatique -- Périodiques; Fabrication -- Périodiques; Manufacturing processes; Production management -- Data processing; Periodicals; 670.5
• DOI: 10.1016/j.jmapro.2015.03.003
• Languages: English
• ISSNs: 1526-6125

Abstract

Abstract: AISI Type 304L austenitic stainless steels are extensively used in industries, and welding is an indispensable tool used for joining these materials. In a multi-pass weld, the development of residual stress to a large extent depends on the response of the weld metal, heat affected zone and parent material to complex thermo-mechanical cycles during welding. Earlier researchers on this area used either mechanical tensioning or heat treatment to modify the residual stress distribution in and around the weld. In this research, microstructural refinement with modification of residual stress state was attempted by using high pressure cold rolling followed by laser processing in 12 mm thick 304L austenitic stainless steels which is a novel technique. The hardening of the weld metal was evaluated after welding, post weld cold rolling, and post weld cold rolling followed by laser processing. The residual stress was determined non-destructively by using neutron diffraction. Residual stress analysis show that post weld cold rolling was effective in modifying the longitudinal residual stress distribution throughout the entire thickness. Post weld cold rolling followed by laser processing performed in this research was to induce recrystallization of the cold rolled grains. However, post weld cold rolling followed by laser processing showed minor grain refinement but was not effective as it reinstated the stress state.