Impact damage tolerance of thermoset composites reinforced with hybrid commingled yarns. (15th April 2016)

• Record Type: Journal Article
• Authors: Selver, Erdem; Potluri, Prasad; Hogg, Paul; Soutis, Costas
• Is Part Of: Composites. Volume 91(2016)
• Page Start: 522
• Page End: 538
• Publication Date: 2016-04-15
• Subjects: A. Hybrid -- A. Fabrics/textiles -- B. Impact behaviour -- B. Damage tolerance -- A. Commingled yarn; Composite materials -- Periodicals; Materials science -- Periodicals; Composite materials; Periodicals; Electronic journals; 620.118
• DOI: 10.1016/j.compositesb.2015.12.035
• Languages: English
• ISSNs: 1359-8368

Abstract

Abstract: This paper examines the potential of low-cost thermoplastic fibres in improving the impact damage resistance and damage tolerance of thermoset (glass-epoxy) composites. Polypropylene (PP) fibres, commodity fibres without any surface modifications, have been incorporated at tow-scale with the aid of air jet commingling process. Glass-PP hybrid yarns with varying proportion of PP fibres (0–35%) are converted into several non-crimp cross-ply laminates and a plain-woven laminate. Damage resistance in terms of damage area and depth are assessed for low energy (20–50 J) as well as high energy (500 J) drop-weight impacts; damage tolerance is assessed through Compression after Impact (CAI) tests. Overall density of the composite laminate has reduced by 16% due to the introduction of PP fibres; at the same time total absorbed energy has increased by 22% during a high velocity impact test due to a toughing mechanism by PP fibres. Non-crimp laminates absorbed more energy at low velocity impacts in comparison to woven laminates, possibly due to extensive tow-level delaminations. On the other hand, a much larger dent depth was observed in the woven laminate after low energy impact. Compression after Impact (CAI) tests indicated that woven laminates retained 83% of compressive strength while non-crimp laminates retained 50–60%, depending on proportion of thermoplastic fibres, and standard glass fibre laminates retain around 45%. Fibre damage has been significantly reduced during impact loading in case of hybrid laminates due to the cushioning effect offered by lower modulus PP fibres.