Evaluation of the photocatalytic degradation of pre-treated palm oil mill effluent (POME) over Pt-loaded titania. Issue 1 (March 2015)

• Record Type: Journal Article
• Authors: Cheng, Chin Kui; Rizauddin Derahman, Mohd; Khan, Maksudur R.
• Is Part Of: Journal of environmental chemical engineering. Volume 3:Issue 1(2015:Mar.)
• Page Start: 261
• Page End: 270
• Publication Date: 2015-03
• Subjects: Photocatalysis -- Platinum -- Palm oil mill effluent (POME) -- Titania -- Wastewater; Chemical engineering -- Environmental aspects -- Periodicals; Environmental engineering -- Periodicals; Chemical engineering -- Environmental aspects; Environmental engineering; Periodicals; 660.0286
• DOI: 10.1016/j.jece.2014.10.016
• Languages: English
• ISSNs: 2213-2929

Abstract

Highlights: XRD confirmed the existence of anatase phase for Pt/TiO2 . XPS showed that Pt existed as Pt 0 and Pt 4+ form. Band gap energy of Pt/TiO2 was 3.16–3.17 eV compared to the TiO2 at 3.20 eV. 0.5 wt% Pt/TiO2 was the best catalyst while maximum loading was 1.0 g/L. Abstract: This paper reports the photocatalytic degradation of pre-treated palm oil mill effluent (POME) over a Pt-doped titania photocatalyst. Pt loading on the titania was varied from 0.25 to 1.0 wt% via alcohol reduction of chloroplatinic acid (H2 PtCl6 ). XRD characterization of the photocatalysts showed that the photo-active anatase phase was still intact after the photocatalyst synthesis while the XPS spectrum confirmed that the deposited Pt was free from the Cl and existed as Pt 0 and Pt 4+ . In addition, the UV–vis diffuse reflectance measurement indicated an improved light energy absorption in the visible light spectrum. Moreover, the band gap energy (3.16–3.17 eV) was reduced when titania was doped with Pt, compared to the pristine titania with 3.20 eV. The 0.5 wt% Pt/TiO2 photocatalyst offered the most effective degradation of pre-treated POME under the irradiation of 100 W of UV light (10%) and also visible light (11%), respectively, over a loading of 0.2 g/L. Significantly, the maximum 0.5 wt% Pt/TiO2 photocatalyst loading determined from the current work was 1.0 g/L.