Novel cardo poly(arylene ether nitrile sulfone) copolymers bearing xanthene moiety in the main chain. (September 2016)

• Record Type: Journal Article
• Authors: Guo, Dong-Dong; Huang, Zhen-Zhong; Sang, Xiao-Yan; Sheng, Shou-Ri
• Is Part Of: High performance polymers. Volume 28:Number 7(2016)
• Page Start: 793
• Page End: 799
• Publication Date: 2016-09
• Subjects: Poly(arylene ether nitrile sulfone) -- copolymer -- xanthene cardo group -- 2, 6-difluorobenzonitrile -- 4 -- 4′-dichlorodiphenylsulfone; Polymerization -- Periodicals; Polymers -- Periodicals; 547.7
• DOI: 10.1177/0954008315597741
• Languages: English
• ISSNs: 0954-0083

Abstract

A series of cardo poly(arylene ether nitrile sulfone) (PENS) copolymers containing xanthene moiety were prepared by the nucleophilic substitution reaction of 9, 9-bis(4-hydroxyphenyl)xanthene with 2, 6-difluorobenzonitrile (DFBN) and 4, 4′-dichlorodiphenylsulfone (DCDPS) by varying stoichiometric ratio of DFBN to DCDPS (90/10–40/60) using N, N -dimethylacetamide (DMAc) as solvent in the presence of anhydrous potassium carbonate. The copolymers having number-average molecular weights of 17, 100–18, 300 g mol −1 with the polydispersity index from 1.79 to 2.11 were amorphous and were easily soluble in polar solvents such as N -methyl-2-pyrrolidone and DMAc, and even in tetrahydrofuran and chloroform at room temperature. The resulting PENS copolymers showed glass transition temperature ( T g ) between 253.3°C and 260.4°C, and the T g values were found to increase with increasing sulfone content in the copolymers. Thermogravimetric studies showed that all the polymers were stable up to 450°C, with 10% weight loss temperatures ranging from 500°C to 524°C and char yields of 56–63% at 700°C under nitrogen atmosphere. All new polymers could be cast into strong and flexible films with tensile strengths of 56.7–78.8 MPa, elongations at break of 7.8–9.1%, and tensile moduli of 2.1–3.2 GPa.