Experimental assessment of thermal grain boundary embrittlement after tubeplate failure in a petrochemical heat exchanger. (September 2017)

• Record Type: Journal Article
• Authors: Otegui, Jose L.; Booman, Janine N.; Massone, Juan
• Is Part Of: Engineering failure analysis. Volume 79(2017)
• Page Start: 140
• Page End: 153
• Publication Date: 2017-09
• Subjects: Tubeplate -- Branched cracks -- Intergranular embrittlement -- Experimental assessment; System failures (Engineering) -- Periodicals; Fracture mechanics -- Periodicals; Reliability (Engineering) -- Periodicals; Pannes -- Périodiques; Rupture, Mécanique de la -- Périodiques; Fiabilité -- Périodiques; Fracture mechanics; Reliability (Engineering); System failures (Engineering); Periodicals; Electronic journals; 620.112
• DOI: 10.1016/j.engfailanal.2017.04.022
• Languages: English
• ISSNs: 1350-6307

Abstract

Abstract: The analysis of multiple cracks in a heat exchanger tubeplate at a petrochemical plant led to experimental replication of in-service damage. High lifting stresses created a first leak that was repaired. Extended branched intergranular cracking developed from the tubeplate surface around the repair weld after few weeks of renewed operation. Chemical analyses failed to detect Na on crack surfaces, while operative conditions also allowed discarding a typical SCC cracking mechanism. Lack of radial interference between tubes and plate, lack of penetration and lack of fusion at tube to tubeplate weld roots were also thought as contributors to cracking. Microstructural analyses revealed martensite clusters in welds and HAZ, and austenite grain boundary precipitates in the tubeplate base material. Thermal cycles were applied to ex-service samples to replicate the conditions for these brittle micro constituents, which were found to be unstable at operating temperatures. Mechanical testing also replicated grain boundary weakness. This inadequate structure was related to welding without proper thermal cycles and heat treatments. Highlights: Conflicting results after the analysis of multiple cracks in a three-stage heat exchanger tubeplate. Microstructural damage near a previous weld repair was experimentally replicated. Failure root causes were related to grain boundary embrittlement due to uncontrolled thermal cycle.