Effect of Texture on the Performance of Mg-air Battery Based on Rolled Mg-3Al-1Zn Alloy Sheet. Issue 4 (April 2018)

• Record Type: Journal Article
• Authors: Yanchun, Zhao; Guangsheng, Huang; Cheng, Zhang; Lin, Chen; Ting-zhuang, Han; Fusheng, Pan
• Is Part Of: Xi you jin shu cai liao yu gong cheng. Volume 47:Issue 4(2018)
• Page Start: 1064
• Page End: 1068
• Publication Date: 2018-04
• Subjects: AZ31 Mg alloy -- texture -- corrosion resistance -- Mg-air battery -- anode efficiency; Nonferrous metals -- Periodicals; 669.05
• DOI: 10.1016/S1875-5372(18)30121-8
• Languages: English
• ISSNs: 1875-5372

Abstract

Abstract : Abstract: Commercial rolled Mg-3Al-1Zn (AZ31) alloy sheet was used as the experimental material, an Mg-air battery based on its rolling surface (RS) and cross-section surface (CS) were both prepared to study the effect of texture on the performance of Mg-air battery. And the experimental samples had a similar surface roughness to practical application. The impedance spectroscopy (EIS) was used to investigate the electrochemical behavior of the samples. The results show that CS surface has a higher corrosion resistance compared with the RS surface. The battery performance was studied by constant current discharge test, and the results show that the Mg-air battery based on the CS surface anode has higher anode efficiency (71.3%) compared with the Mg-air battery based on the RS surface anode (65.7%). The surface morphologies of the magnesium alloy anodes substrate after discharged for 24 h were observed by scanning electron microscope. The RS anode exhibits a magnesium alloy anode substrate with more holes and gullies, which may contribute to its lower anode efficiency. Thus, the CS anode dominated by (10 1 ¯ 0), (11 2 ¯ 0) and (10 1 ¯ 1) orientated grains is more suitable to use on Mg-air battery.