Investigation on the thermostability of residual stress and microstructure in shot peened SAF 2507 duplex stainless steel. (July 2018)

• Record Type: Journal Article
• Authors: Chen, Ming; Liu, Huabing; Wang, Lianbo; Xu, Zhou; Ji, Vincent; Jiang, Chuanhai
• Is Part Of: Vacuum. Volume 153(2018)
• Page Start: 145
• Page End: 153
• Publication Date: 2018-07
• Subjects: Thermally activated relaxation -- Shot peening -- Duplex stainless steel -- XRD; Vacuum -- Periodicals; 621.55
• DOI: 10.1016/j.vacuum.2018.04.015
• Languages: English
• ISSNs: 0042-207X

Abstract

Abstract: SAF 2507 duplex stainless steels were treated by shot peening (SP) and then isothermally annealed at elevated temperatures (600–750 °C). The thermal stability of surface residual stress and microstructure of shot peened material were investigated. Results showed that most of the stress relaxation took place within the initial 30 min, and the relaxation behavior could be described by the Zener-Wert-Avrami function. The derived activation energies of stress relaxation for γ and α phase were close to the vacancy-migration-energy in iron. γ phase exhibited higher stress and microstrain relaxation rate than α phase, which was ascribed to the higher stored energy in γ phase. A heavy reduction in dislocations and dislocation cells accompanying with the growth of subgrains was observed in the recrystallized microstructure. The recrystallized grains formed in γ phase were much finer than that in α phase. Moreover, SP accelerated the precipitation kinetics of σ phase, a mass of σ phase was precipitated in the deformed layer after isothermal annealing. Highlights: Thermostability of residual stress and microstructure of shot peened SAF 2507 steel was studied. The stress relaxation rate in γ phase was much higher than that in α phase. The activation energies of the stress relaxation were about 67 and 62 kJ/mol for γ and α phase. Shot peening accelerated the precipitation kinetics of σ phase.