Photovoltaic solar panels of crystalline silicon: Characterization and separation. Issue 3 (March 2016)

• Record Type: Journal Article
• Authors: Dias, Pablo Ribeiro; Benevit, Mariana Gonçalves; Veit, Hugo Marcelo
• Is Part Of: Waste management & research. Volume 34:Issue 3(2016:Mar.)
• Page Start: 235
• Page End: 245
• Publication Date: 2016-03
• Subjects: Solar panel -- crystalline silicon -- recycling -- characterization; Factory and trade waste -- Periodicals; Refuse and refuse disposal -- Periodicals; Municipal engineering -- Periodicals; Déchets industriels -- Périodiques; Déchets -- Élimination -- Périodiques; Génie urbain -- Périodiques; 628
• DOI: 10.1177/0734242X15622812
• Languages: English
• ISSNs: 0734-242X

Abstract

Photovoltaic panels have a limited lifespan and estimates show large amounts of solar modules will be discarded as electronic waste in a near future. In order to retrieve important raw materials, reduce production costs and environmental impacts, recycling such devices is important. Initially, this article investigates which silicon photovoltaic module's components are recyclable through their characterization using X-ray fluorescence, X-ray diffraction, energy dispersion spectroscopy and atomic absorption spectroscopy. Next, different separation methods are tested to favour further recycling processes. The glass was identified as soda-lime glass, the metallic filaments were identified as tin–lead coated copper, the panel cells were made of silicon and had silver filaments attached to it and the modules' frames were identified as aluminium, all of which are recyclable. Moreover, three different components segregation methods have been studied. Mechanical milling followed by sieving was able to separate silver from copper while chemical separation using sulphuric acid was able to detach the semiconductor material. A thermo gravimetric analysis was performed to evaluate the use of a pyrolysis step prior to the component's removal. The analysis showed all polymeric fractions present degrade at 500 °C.