Effect of hot working on the damping capacity and mechanical properties of AZ31 magnesium alloy. Issue 1 (April 2015)

• Record Type: Journal Article
• Authors: Lee, K; Kang, C; Kim, K
• Is Part Of: IOP conference series. Volume 82:Issue 1(2015)
• Publication Date: 2015-04
• Subjects: Materials science -- Periodicals; 620.1105
• DOI: 10.1088/1757-899X/82/1/012114
• Languages: English
• ISSNs: 1757-8981

Abstract

Abstract: Magnesium alloys have received much attention for their lightweight and other excellent properties, such as low density, high specific strength, and good castability, for use in several industrial and commercial applications. However, both magnesium and its alloys show limited room-temperature formability owing to the limited number of slip systems associated with their hexagonal close-packed crystal structure. It is well known that crystallographic texture plays an important role in both plastic deformation and macroscopic anisotropy of magnesium alloys. Many authors have concentrated on improving the room- temperature formability of Mg alloys. However, despite having a lot of excellent properties in magnesium alloy, the study for various properties of magnesium alloy have not been clarified enough yet. Mg alloys are known to have a good damping capacity compared to other known metals and their alloys. Also, the damping properties of metals are generally recognized to be dependent on microstructural factors such as grain size and texture. However, there are very few studies on the relationship between the damping capacity and texture of Magnesium alloys. Therefore, in this study, specimens of the AZ31 magnesium alloy, were processed by hot working, and their texture and damping property investigated. A 60 mm × 60 mm × 40 mm rectangular plate was cut out by machining an ingot of AZ31 magnesium alloy (Mg-3Al-1Zn in mass%), and rolling was carried out at 673 K to a rolling reduction of 30%. Then, heat treatment was carried out at temperatures in the range of 573-723 K for durations in the range of 30-180 min. The samples were immediately quenched in oil after heat treatment to prevent any change in the microstructure. Texture was evaluated on the compression planes by the Schulz reflection method using nickel-filtered Cu Kα radiation. Electron backscatter diffraction measurements were conducted to observe the spatial distribution of various orientations. Specimens for damping capacity measurements were machined from the rolled specimen, to have a length of 120 mm, width of 20 mm, and thickness of 1 mm. The damping capacity was measured with a flexural internal friction measurement machine at room temperature. It was found that the damping capacity increases with both increasing heat-treatment temperature and time, due to grain growth and the increased pole densities of textures.