Preparation of kaolinite nanotubes by a solvothermal method. Issue 5 (June 2015)

• Record Type: Journal Article
• Authors: Xu, Hongliang; Jin, Xiaozeng; Chen, Pei; Shao, Gang; Wang, Hailong; Chen, Deliang; Lu, Hongxia; Zhang, Rui
• Is Part Of: Ceramics international. Volume 41:Issue 5(2015)Part A
• Page Start: 6463
• Page End: 6469
• Publication Date: 2015-06
• Subjects: D. Clays -- Kaolinite nanotubes -- Intercalation -- Solvothermal reaction; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2015.01.085
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Kaolinite nanotubes were prepared by intercalation and solvothermal reactions using pristine kaolin as a starting material. Firstly, an intercalation compound of kaolinite/dimethyl sulfoxide was prepared as a precursor. Then, kaolinite/methanol (KM) was achieved by replacing dimethyl sulfoxide with methanol through solvothermal reaction at 100 °C. Dimethyl sulfoxide molecules can be replaced mostly when the reaction time was 2 h, and the intercalation ratio of KM compound reached 97.9% for the reaction time of 24 h. Finally, the kaolinite nanotubes were achieved by the solvothermal reaction of the KM compound and methanol solution of CTAC (1 M) at 100 °C for 24 h. XRD, IR, SEM, and N2 sorption measurements were used to characterize the as-prepared samples. It is found that the kaolinite nanotubes had a specific surface area of 45.44 m 2 /g. The length of the nanotubes is about 300–2000 nm and the internal diameter and external diameter is about 15–55 nm and 40–80 nm, respectively.