Pillaring of layered zeolite precursors with ferrierite topology leading to unusual molecular sieves on the micro/mesoporous border. Issue 9 (13th November 2017)

• Record Type: Journal Article
• Authors: Roth, Wieslaw J.; Gil, Barbara; Mayoral, Alvaro; Grzybek, Justyna; Korzeniowska, Aleksandra; Kubu, Martin; Makowski, Wacław; Čejka, Jiří; Olejniczak, Zbigniew; Mazur, Michal
• Is Part Of: Dalton transactions. Volume 47:Issue 9(2018)
• Page Start: 3029
• Page End: 3037
• Publication Date: 2017-11-13
• Subjects: Chemistry, Inorganic -- Periodicals; Chemistry, Physical and theoretical -- Periodicals; Chemistry, Inorganic -- Periodicals; 546.05
• DOI: 10.1039/c7dt03718j
• Languages: English
• ISSNs: 1477-9226

Abstract

Abstract : Pillaring of FER layers gives porous products depending on the temperature of TEOS treatment. Abstract : Layered zeolite materials with FER layer topology can produce various condensed and expanded structures including zeolite frameworks, FER and CDO, their interlayer expanded forms (IEZ), and organic-intercalated and pillared derivatives. This work concerns pillaring of the surfactant-swollen derivative with a gallery height of ca. 2.5 nm between layers by treatment with tetraethylorthosilicate (TEOS) at room and elevated temperatures. The materials obtained at 100 °C and higher showed unusual properties including 2 nm pores on the micro/mesoporous border and disordered layer packing indicated by the absence of distinct low angle interlayer peaks at d -spacing >3 nm (∼3° 2 θ Cu Kα radiation) in the X-ray diffraction pattern (XRD). TEOS treatment at room temperature produced a pillared molecular sieve with the expected mesoporous characteristics, namely a pore size of around 3 nm and a high intensity low angle (001) peak at 2.3° 2 θ, and a d -spacing of 3.8 nm, in the XRD. The characterization aiming to elucidate the nature of the obtained unusual products included gas adsorption isotherms, aberration corrected ( C s -corrected) Scanning Transmission Electron Microscopy (STEM) studies and 29 Si solid state NMR. BET surface area values decreased with the temperature of TEOS treatment from approximately 1200 m 2 g −1 to ∼900 and 600 m 2 g −1, at room temperature, 100 °C, and 120 °C, respectively. The 29 Si solid state NMR revealed the presence of both Q 3 ((SiO)3 SiOX, X = H or minus charge) and Q 4 ((SiO)4 Si) centers giving separated signals up to the pillaring step. After pillaring at 100 °C and calcination, the nominal intensity ratios Q 4 : Q 3 were 2.17 and 2.61 but the signals were merged into one broad peak indicating the structural heterogeneity of Si–O coordination. The microscopy showed the presence of FER layers in the samples but the overall structure and composition were not well-defined. The observed unusual disorganization and possible partial degradation of layers during pillaring may result from the combination of high temperature, alkalinity (surfactant hydroxide) and siliceous composition of the layers. The obtained pillared products are of interest for the preparation of larger pore catalysts and sorbents or controlled drug delivery.