Effect of layer sequence on the mechanical properties of Ti/TiAl laminates. (5th April 2018)

• Record Type: Journal Article
• Authors: Lyu, Shaoyuan; Sun, Yanbo; Li, Guodong; Xiao, Wenlong; Ma, Chaoli
• Is Part Of: Materials & design. Volume 143(2018)
• Page Start: 160
• Page End: 168
• Publication Date: 2018-04-05
• Subjects: TiAl -- Laminates -- Microstructure -- Tensile properties -- Calculations; Materials -- Periodicals; Engineering design -- Periodicals; Matériaux -- Périodiques; Conception technique -- Périodiques; Electronic journals; 620.11
• DOI: 10.1016/j.matdes.2018.02.003
• Languages: English
• ISSNs: 0264-1275

Abstract

Abstract: The Ti/TiAl metal-intermetallic laminates were fabricated by hot-pressing starting from the elemental Ti and Al foils. The final microstructures of laminates consist of alternating layers of ductile Ti and brittle intermetallic. The relationships between mechanical properties and layer sequence of Ti/TiAl laminates have been studied by examining the effects of solid solubility of Al in Ti layer, the volume fraction of intermetallic layer and the interlayer spacing. In these three cases, the samples with the best performance are obtained and among them the optimal sample is confirm with fracture strength 752 MPa, K IC 48 MPa·m 1/2 . In particularly, a novel theoretical formula of strength calculation is proposed according to the mixing rule of composites. The theoretically calculated results agree well with the experimental results. Highlights: The fracture strength increases first and then decreases with increasing the Al content in Ti layer. When Ti volume is constant, the fracture strength decreases with increasing the volume fraction of intermetallic. The fracture strength increases first and then decreases with increasing the interlayer spacing. A novel formula is proposed about failure strength and calculated results agree well with experimental results. Graphical abstract: