A failure study of a locking compression plate implant. (April 2015)

• Record Type: Journal Article
• Authors: Thapa, Nirajan; Prayson, Michael; Goswami, Tarun
• Is Part Of: Case studies in engineering failure analysis. Volume 3(2015)
• Page Start: 68
• Page End: 72
• Publication Date: 2015-04
• Subjects: Locking compression plate -- Screws -- Striations -- Intermetallic inclusion -- Beach marks -- Corrosion; System failures (Engineering) -- Case studies -- Periodicals; Fracture mechanics -- Case studies -- Periodicals; Fracture mechanics; Reliability (Engineering); System failures (Engineering); Electronic journals -- Sciences; Case studies; Periodicals; 620.0045205
• DOI: 10.1016/j.csefa.2015.03.004
• Languages: English
• ISSNs: 2213-2902

Abstract

Highlights: In addition to the static loads, cyclic loading acting on the construct caused the earlier failure. Initiation of crack from the area of intermetallic inclusions. Striation spacing versus crack length was determined. Abstract: In this case study a failed locking compression plate was investigated. Such plating systems are used to provide the stability to fractured bone and fixation. The locking compression plate had been separated in two pieces. One of the fracture surfaces from the failed component was investigated for surface topographical features. The visual, optical and scanning electron microscopy results indicated the presence of beach marks, intermetallic inclusions, corrosion pits and striations indicating fatigue crack propagation and overload failure. Some corrosion damage also was documented on the fractography. This case study shows that corrosion may have initiated fatigue crack which grew by the activities of daily living causing the failure.