Surface-coating synthesis of nitrogen-doped inverse opal carbon materials with ultrathin micro/mesoporous graphene-like walls for oxygen reduction and supercapacitors. Issue 48 (27th November 2017)

• Record Type: Journal Article
• Authors: Yao, Yan; Chen, Zhi; Zhang, Aijian; Zhu, Jiahui; Wei, Xiangru; Guo, Jun; Wu, Winston Duo; Chen, Xiao Dong; Wu, Zhangxiong
• Is Part Of: Journal of materials chemistry. Volume 5:Issue 48(2018)
• Page Start: 25237
• Page End: 25248
• Publication Date: 2017-11-27
• Subjects: Materials -- Research -- Periodicals; Chemistry, Analytic -- Periodicals; Environmental sciences -- Research -- Periodicals; 543.0284
• DOI: 10.1039/c7ta08354h
• Languages: English
• ISSNs: 2050-7488

Abstract

Abstract : A surface-coating templating method is adopted to construct 3D hierarchical carbons with ultrathin graphene-like walls for the high-performance ORR and supercapacitors. Abstract : Hierarchical carbon materials are highly attractive for energy storage and conversion. To improve their performances in electrocatalytic oxygen reduction and supercapacitors, the construction of 3D ordered macroporous frameworks built from ultrathin micro/mesoporous nitrogen-doped graphene-like walls is proposed to enrich accessible active sites and shorten the mass and electron transport paths. A surface-coating hard-templating method is developed for this purpose. The synthesis involves packing silica nanospheres into an opal, designed surface coating with histidine, carbonizing and template removal. The strong adhesive binding between silica and histidine and cohesive interactions among histidine molecules direct the uniform coating and subsequent formation of ultrathin (∼2.8 nm) carbon layers. Various N-doped inverse opal carbons (N-IOCs) with ordered macropores, graphene-like walls, high surface areas up to ∼1365 m 2 g −1, narrow micro/mesopores of 0.6–5.0 nm, and high N content up to ∼14.72 wt% are obtained. The optimized N-IOCs exhibit outstanding performances in the oxygen reduction reaction with extraordinary activities, up to 0.95 and 0.87 V for the onset and half-wave potentials, which are among the best for heteroatom-doped carbon materials reported thus far, and excellent methanol tolerance and stability, as well as showing high capacitances of up to 222 F g −1 and good rate capability and stability in supercapacitors. Control experiments reveal that the remarkable performance is ascribed to the ordered macropores for rapid mass transportation, the ultrathin carbon layers for fast electron transfer, and the high surface areas for hosting abundant active sites.