Fluoride degradable and thermally debondable polyurethane based adhesive. Issue 46 (14th November 2017)

• Record Type: Journal Article
• Authors: Babra, Tahkur Singh; Trivedi, Akash; Warriner, Colin N.; Bazin, Nicholas; Castiglione, Dario; Sivour, Clive; Hayes, Wayne; Greenland, Barnaby W.
• Is Part Of: Polymer chemistry. Volume 8:Issue 46(2017)
• Page Start: 7207
• Page End: 7216
• Publication Date: 2017-11-14
• Subjects: Polymers -- Periodicals; Macromolecules -- Periodicals; Polymerization -- Periodicals; 547.705
• DOI: 10.1039/c7py01653k
• Languages: English
• ISSNs: 1759-9954

Abstract

Abstract : A polyurethane-based adhesive has been produced that can undergo multiple thermal debonding/bonding cycles and also irreversibly debond through depolymerisation on contact with fluoride ions. Abstract : We report the one-pot, solvent free synthesis of a stimuli-responsive polyurethane (PU) adhesive. The hard domains within the supramolecular PU network contain a silyl protected phenol 'degradable unit' (DU). The DU undergoes rapid decomposition (<30 minutes) upon treatment with fluoride ions which causes depolymerisation of the linear PU adhesive. The mechanism of depolymerisation was investigated in solution using 1 H NMR spectroscopy by following the degradation of the polymer in the presence of tetra -butylammonium fluoride (TBAF). In the absence of fluoride ions, the material behaves as a typical thermoplastic adhesive, and underwent four adhesion/separation cycles without loss of strength. The fluoride initiated depolymerisation of the PU adhesive in the solution state was verified by GPC analysis, showing reduction in M n from 26.1 kg mol −1 for the pristine PU to 6.2 kg mol −1 for the degraded material. Degradation studies on solid samples of the PU which had been immersed in acetone/TBAF solution for 30 minutes exhibited a 91% reduction in their modulus of toughness (from 27 to 2 MJ m −3 ). Lap shear adhesion studies showed the fluoride responsive PU was an excellent material to join metallic, plastic, glass and wood surfaces. Pull adhesion tests confirmed that immersing the adhesive in TBAF/acetone solution resulted in a reduction in strength of up to 40% (from 160 N to 95 N at break) after drying.