The mechanism of NOx emissions from binary molten nitrate salts contacting nickel base alloy in thermal energy storage process. (1st December 2017)

• Record Type: Journal Article
• Authors: Wei, Xiaolan; Yang, Chuntao; Lu, Jianfeng; Wang, Weilong; Ding, Jing
• Is Part Of: Applied energy. Volume 207(2017)
• Page Start: 265
• Page End: 273
• Publication Date: 2017-12-01
• Subjects: Binary molten nitrate salts -- NOx emissions -- Nickel base alloy; Power (Mechanics) -- Periodicals; Energy conservation -- Periodicals; Energy conversion -- Periodicals; 621.042
• DOI: 10.1016/j.apenergy.2017.06.109
• Languages: English
• ISSNs: 0306-2619

Abstract

Highlights: The effect of In600, Has X, In625 and HasC 276 on NO x emissions was studied. Chemical thermodynamic of reactions were calculated to study the mechanism of NO x emission. NO x emission was reduced for treated In625 and HasC 276 due to the oxide film formation. Abstract: This work aimed at investigating the mechanism of NO x emissions from binary molten nitrate (BMN) salts (an eutectic salt mixture with the component of 60%NaNO3 -40%KNO3 ) in its thermal energy storage (TES) process while contacting several kinds of nickel base alloy and determining the optimized temperature range of BMN salts in these metal loops. According to the national environmental protection standard of PR China, HJ479-2009, the concentrations of NO/NO2 net emissions in tail gases from the heated molten salts while contacting with Inconel 625 (In625), Hastelloy C276 (HasC 276), Hastelloy X (Has X) and Inconel 600 (In600) were measured in TES process, which were deducted the influence of platinum boat while contacting with the molten nitrates. Besides, the In625 and HasC 276 were chosen to test with the same method at 500 °C under the condition that they were corroded at 500 °C after a period of time, SEM/EDS and XRD techniques were utilized to study the surface morphology and corrosion products after a maximum immersion time of 600 h. Furthermore, the chemical thermodynamic calculations of related reactions that between Cr, Ni, Mo, W and nitrate salts were carried out to explain the source of NO/NO2 . The test results show that BMN salts contained in pipes or tanks made of nickel base alloy under air atmosphere in certain conditions can release NO x in its usage temperature range, and the concentrations of NO x emissions increase with the rise of the temperature. Below 500 °C, the concentrations of NO x net emissions that BMN salts contacting with these four kinds of nickel base alloys were under 200 mg/m 3, which is in accordance with the emission limit of thermal power plant in China and the emission limit of second directive of EU in coal-fired power plant. Besides, the concentrations of NO x emissions that BMN salts contacting with corrode materials would decrease to some extent. After a period of corrosion, the formed oxide film on metal surface was very thin but dense. Therefore, the BMN salts were advisable to utilize under 500 °C at the initial stage, and it can be used at higher temperature after the stable oxide film formed in the metal surface.