Effect of tensile dwell on high-temperature low-cycle fatigue and fracture behaviour of cast superalloy MAR-M247. (November 2017)

• Record Type: Journal Article
• Authors: Šulák, Ivo; Obrtlík, Karel
• Is Part Of: Engineering fracture mechanics. Volume 185(2017)
• Page Start: 92
• Page End: 100
• Publication Date: 2017-11
• Subjects: Nickel-based superalloy -- High-temperature low-cycle fatigue -- Tensile dwell -- Fatigue life -- Damage mechanisms; Fracture mechanics -- Periodicals; Rupture, Mécanique de la -- Périodiques; Fracture mechanics; Periodicals; 620.112605
• DOI: 10.1016/j.engfracmech.2017.04.002
• Languages: English
• ISSNs: 0013-7944

Abstract

Highlights: Low-cycle fatigue properties of polycrystalline Ni-based superalloy MAR-M247. Effect of tensile dwell on stress-strain response and fatigue life at 900 °C. Damage mechanisms both in continuous cycling and in cycling with dwells. Abstract: Hot isostatically-pressed, nickel-based superalloy MAR-M247 was tested under fatigue and creep-fatigue conditions. Continuous cycling and cycling with 10 min tensile dwells in each cycle were applied in symmetrical strain control cycle with constant total strain amplitude at 900 °C in air. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained. The introduction of tensile dwells resulted in lower fatigue life in total strain representation. Surface relief, specimen sections and fracture surface observations revealed crack initiation sites, crack density and crack paths, and help to clarify the effect of dwells on fatigue behaviour.