Ferrocene-based porous organic polymer derived high-performance electrocatalysts for oxygen reduction. Issue 42 (19th October 2017)

• Record Type: Journal Article
• Authors: Zhou, Baolong; Liu, Liangzhen; Cai, Pingwei; Zeng, Guang; Li, Xiaoqiang; Wen, Zhenhai; Chen, Long
• Is Part Of: Journal of materials chemistry. Volume 5:Issue 42(2017)
• Page Start: 22163
• Page End: 22169
• Publication Date: 2017-10-19
• Subjects: Materials -- Research -- Periodicals; Chemistry, Analytic -- Periodicals; Environmental sciences -- Research -- Periodicals; 543.0284
• DOI: 10.1039/c7ta06515a
• Languages: English
• ISSNs: 2050-7488

Abstract

Abstract : Two nitrogen-rich porous organic polymers (POPs) were prepared via Schiff base chemistry. Carbonization of these POPs results in porous carbon nanohybrids which exhibit excellent catalytic activity toward the oxygen reduction reaction (ORR). Abstract : Two nitrogen-rich porous organic polymers (POPs) were prepared via facile and low-cost Schiff base chemistry with ferrocene (Fc) and melamine/melem as building blocks. Carbonization of these POP precursors results in porous carbon nanohybrids with carbon composites containing crystalline Fe3 C/Fe. Characterization based on a variety of techniques demonstrates that the porous carbon nanohybrids feature rich-nitrogen doping, good conductivity and high BET surface area with unique porous structure, endowing them with an excellent catalytic activity toward the oxygen reduction reaction (ORR) in alkaline electrolytes. The catalysts obtained by carbonization at 800 °C (N-Fc-800) exhibit favorable activity with a rather high onset potential and half wave potential of 0.96 and 0.82 V, respectively. Furthermore, a rechargeable zinc-air battery was assembled using the N-Fc-800 as the cathode catalyst. Compared with the commercial Pt/C, the N-Fc-800 based battery displays a considerably high power density of 178 mW cm −2 with a smaller charge–discharge voltage gap of 0.94 V, and holds excellent stability with a less activity decay (1.0%) over long charge–discharge cycles (200 cycles).