Relationship between initial and time-dependent cracks in charge transport of solution-processed organic thin-film transistor. (13th August 2017)

• Record Type: Journal Article
• Authors: Jung, Ji-Hoon; Kim, Young-Rae; Choe, Eunji; Song, Dong-Seok; Bae, Jin-Hyuk
• Is Part Of: Molecular crystals and liquid crystals. Volume 653(2017)
• Page Start: 238
• Page End: 242
• Publication Date: 2017-08-13
• Subjects: Crack -- organic semiconductor -- solution-process -- thin-film -- transistor; Molecular crystals -- Periodicals; Liquid crystals -- Periodicals; Liquid crystals; Molecular crystals; Periodicals; 548
• DOI: 10.1080/15421406.2017.1352437
• Languages: English
• ISSNs: 1542-1406

Abstract

ABSTRACT: We report on the comprehensive effect of initial and time-dependent crack on the charge transport of 6, 13-bis (triisopropylsilyethynyl) pentacene (TIPS-PEN) thin-film transistors (TFTs) upon exposure to air. Among the two types of TIPS-PEN films, with and without initial thermal cracks, temporally generated cracks were found to be severely affected by the initial status of the thermal cracks upon air-exposure. After 12 months of air-exposure, the charge transport characteristics of TIPS-PEN TFTs with initial thermal cracks degraded up to 98%, while those without initial thermal cracks degraded only 88%. Based on our long-term experimental results, we conclude that the initial physical status of the cracks play a significant role in the growth of time-dependent cracks and the capability of charge transport in solution-processed TFTs.