Tensile fracture behavior and strength distribution of SiCf/SiC composites with different SiBN interface thicknesses. Issue 1 (January 2015)

• Record Type: Journal Article
• Authors: Liu, Yongsheng; Chai, Nan; Qin, Hailong; Li, Zan; Ye, Fang; Cheng, Laifei
• Is Part Of: Ceramics international. Volume 41:Issue 1(2015)Part B
• Page Start: 1609
• Page End: 1616
• Publication Date: 2015-01
• Subjects: Borosilicate nitride interface -- Ceramic matrix composite -- Chemical vapor infiltration -- Fracture behavior -- Strength distribution; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2014.09.098
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: The borosilicate nitride (SiBN) interface was firstly fabricated in SiC fibers reinforced SiC matrix (SiCf /SiC) composites by low-pressure chemical vapor infiltration (LPCVI). Tensile fracture behavior and strength distribution of SiCf /SiC composites with different SiBN thicknesses were investigated. The results showed that the tensile strength first increased and then declined with increasing interface thickness. The maximum value of tensile strength was 550.8 MPa with a 1000 nm SiBN interface. Non-brittle tensile fracture behavior of SiCf /SiC composites with a SiBN interface was demonstrated. The pull-out length and amount of fibers had a similar variation trend with increasing interface thickness. Strength distributions of SiCf /SiC composites with different interface thicknesses followed Weibull distribution with two parameters. Weibull modules of tensile strength increased first, and then decreased with increasing interface thickness. The maximum value of the Weibull module was 11.0224 when the interface thickness was 1000 nm, which indicated the highest reliability of SiCf /SiC composites. The mean value of tensile strength for SiCf /SiC composite with 1000 nm interface was 576.82 MPa obtained by the theory calculation, which was consistent with the result of experiment (550.8 MPa) very well.