1.53 µm luminescence properties of Er3+-doped K–Sr–Al phosphate glasses. Issue 4 (May 2015)

• Record Type: Journal Article
• Authors: Linganna, K.; Rathaiah, M.; Vijaya, N.; Basavapoornima, Ch.; Jayasankar, C.K.; Ju, S.; Han, W.-T.; Venkatramu, V.
• Is Part Of: Ceramics international. Volume 41:Issue 4(2015)
• Page Start: 5765
• Page End: 5771
• Publication Date: 2015-05
• Subjects: Er3+ ion -- Phosphate glasses -- Judd–Ofelt analysis -- Radiative properties -- Stimulated emission cross-section; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2014.12.162
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Trivalent erbium (Er 3+ )-doped K–Sr–Al phosphate glasses were prepared and studied their spectroscopic properties as a function of Er2 O3 concentration. Judd–Ofelt analysis has been carried out for 1.0 mol% Er2 O3 -doped phosphate glass and in turn radiative properties have been evaluated for the excited levels of Er 3+ ion. The radiative lifetime for the 4 I13/2 level was found to be higher for the present glass when compared to other Er 3+ -doped glasses. The Er 3+ -doped glasses exhibit intense near infrared emission at 1.53 µm corresponds to 4 I13/2 → 4 I15/2 transition as well as green emission at 546 nm corresponding to 4 S3/2 → 4 I15/2 under 980 nm and 488 nm excitations, respectively. The emission cross-section spectrum for 1.0 mol% of Er2 O3 -doped glass has been evaluated using McCumber theory. The gain cross-section has been evaluated as a function of population inversion, which revealed that the lasing action would be achieved at 1.53 µm for a population inversion about 40%. Decay curves for the 4 I13/2 level were measured and lifetimes have been determined for the studied glasses. The results indicate that the present glasses could be useful for laser as well as optical amplifiers at 1.53 µm.