Low Loss, High NA Chalcogenide Glass Fibers for Broadband Mid‐Infrared Supercontinuum Generation. Issue 5 (26th March 2015) - Zhang, Bin
Abstract : High‐purity Ge–As–Se and Ge–As–S chalcogenide glasses were prepared by modified physical and chemical purification techniques. Using the purified glasses, step‐index fibers with a small core (~5.5 μm) and large numerical aperture (~1.3) were fabricated. When a 13.5‐cm‐long fiber was pumped with 320 fs pulses at a repetition rate of 10.5 MHz at 4.1 μm, supercontinuum spanning from ~1.8 to ~9.8 μm with a dynamic range of ±10 dB and an average power of ~3 mW was generated.