Effects of elements W and C on microstructure and wear property of γ-TiAl surface alloying layer. (6th October 2014)

• Record Type: Journal Article
• Authors: Duan, B. Z.; Zhang, P. Z.; Wei, X. F.; Wang, L.; Wei, D. B.; Zhen, D. D.
• Is Part Of: Surface engineering. Volume 31:Number 12(2015)
• Page Start: 942
• Page End: 948
• Publication Date: 2014-10-06
• Subjects: Double glow plasma surface alloying technique -- TiAl based alloy -- Wear resistance -- H/E and H3/E2 ratios; Surfaces (Technology) -- Periodicals; Coatings -- Periodicals; 620.4405
• DOI: 10.1179/1743294414Y.0000000386
• Languages: English
• ISSNs: 0267-0844

Abstract

Abstract : To solve the poor tribological property of the γ-TiAl alloy, the duplex treatment of plasma carburisation on plasma alloying γ-TiAl with tungsten was conducted by double glow plasma surface alloying technique. The results indicated the alloying layer consisted of TiC and W2 C phase, metallurgically adhered to the substrate. In terms of the H/E and H 3 /E 2 ratios, the duplex treated specimen was nearly three times larger than the untreated specimen. The wear property of the specimens was tested on a pin-on-disk tribometer by rubbing against Si3 N4 ceramic ball. The wear rate of the duplex-treated specimens is 1·056×10 −4 mm 3 N −1 m −1, which is only 25·9% of that of the untreated specimens. The relationship between alloying layer mechanical property and wear resistance indicates that the carbide phase formed within the alloying layer contributes to the improvement of the wear performance.