Effect of the stress ratio on the fatigue behavior of Zr55Al10Ni5Cu30 bulk metallic glass part I — Analysis of the fatigue resistance. (January 2018)

• Record Type: Journal Article
• Authors: Guennec, Benjamin; Nobori, Takuya; Kuwahara, Hirotaka; Ueno, Akira
• Is Part Of: Intermetallics. Volume 92(2018:Jan.)
• Page Start: 72
• Page End: 78
• Publication Date: 2018-01
• Subjects: Metallic glasses -- Fatigue resistance and crack growth -- Toughness; Intermetallic compounds -- Metallography -- Periodicals; Metallic glasses -- Periodicals; Composés intermétalliques -- Métallographie -- Périodiques; 669.94
• DOI: 10.1016/j.intermet.2017.09.023
• Languages: English
• ISSNs: 0966-9795

Abstract

Abstract: In the field of innovative material processing, researches dealing with the mechanical properties of Bulk Metallic Glasses (BMGs) are incontestably one of the most topical issues in the latest years. Indeed, this type of materials presents some very interesting properties, such as a high yield stress, a noticeable elongation at fracture and a good corrosion resistance. Thus, it is though that, in a near future, metallic glasses would be able to fulfill structural material applications, which are currently restricted to conventional crystalline metallic materials. However, it is already known that BMGs usually show poor fatigue properties compared to its crystalline counterparts, reducing the actual use of BMGs to non-structural applications. Thus, such promising usages require a better understanding of the fatigue properties of BMGs, explaining the numerous works carried out to overcome this difficulty. Surprisingly, only a few literature reports are focused on the effect of the stress ratio R (= σ min / σ max ) on the high-cycle fatigue behavior of BMGs. In the present work, the effect of the stress ratio, up to R = 0.7, on both the fatigue properties and fatigue crack propagation behavior of Zr55 Al10 Ni5 Cu30 BMG have been studied. This first part is dealing with the fundamental fatigue resistance investigated at three distinct stress ratios of R = 0.1, 0.4 and 0.7. In addition, some discussions related to fracture observation will be discussed, revealing an irregularity of the fatigue crack propagation mechanism at R = 0.7. Finally, relative influences of both stress range and maximum stress level were analyzed using a phenomenological law. Highlights: Effect of stress ratio R was studied in the range from 0.1 to 0.7. Fatigue limit at 10 7 cycles is almost insensitive to stress ratio. K max influence on fatigue life overcomes Δ K one at R = 0.7. Specific "gutter-like" patterns are found on the fracture surface at R = 0.7. Cyclic- and time-dependency of fatigue behavior were analyzed.