Fatigue performance of biodegradable magnesium–calcium alloy processed by laser shock peening for orthopedic implants. (January 2016)

• Record Type: Journal Article
• Authors: Sealy, M.P.; Guo, Y.B.; Caslaru, R.C.; Sharkins, J.; Feldman, D.
• Is Part Of: International journal of fatigue. Volume 82:Part 3(2016)
• Page Start: 428
• Page End: 436
• Publication Date: 2016-01
• Subjects: Surface treatment -- Fatigue -- Magnesium -- Biodegradable implant -- Laser shock peening; Materials -- Fatigue -- Periodicals; Materials -- Fatigue; Periodicals; 620.1122
• DOI: 10.1016/j.ijfatigue.2015.08.024
• Languages: English
• ISSNs: 0142-1123

Abstract

Graphical abstract: Highlights: Laser shock peening (LSP) was implemented on a biodegradable MgCa alloy to measure the effect on fatigue life. The LSP prolonged fatigue life was attributed to the enhanced surface integrity. Higher overlap ratios during LSP further prolonged fatigue life. Abstract: Permanent orthopedic implants made from titanium, stainless steel, or cobalt–chromium alloys cause stress shielding and lead to secondary surgery. Biodegradable magnesium–calcium (MgCa) alloys have the potential to minimize stress shielding as well as eliminate the need for secondary surgery. The critical technical challenge is that magnesium degrades rapidly in the human body. In order to slow the corrosion rate, surface treatments such as laser shock peening (LSP), shot peening, or burnishing have been reported in literature. Each of these surface treatments uniquely alters the surface integrity and consequent fatigue life. Even though surface treatments may be effective at slowing corrosion rates, it is important to ensure that they do not shorten fatigue life. The purpose of this study was to (1) develop a laser shock peening (LSP) surface treatment of a curved surface that adjusts the surface integrity of a MgCa alloy by varying the peening overlap ratio and (2) determine the effect of LSP on the fatigue life. Surface integrity was characterized by topography, microstructure, and microhardness. Fatigue life of laser peened and unpeened samples were measured by rotating bending fatigue tests. It was found that LSP increased the fatigue life of the peened MgCa samples. Implementing LSP at high overlap ratios reduced the surface pile-up which resulted in a higher fatigue life. The fractured surfaces of the peened samples exhibited striation patterns which were more pronounced at higher peening overlap ratios.