Use of calcium sulfoaluminate cements for setting control of 3D-printing mortars. (30th December 2017)

• Record Type: Journal Article
• Authors: Khalil, Noura; Aouad, Georges; El Cheikh, Khadija; Rémond, Sébastien
• Is Part Of: Construction & building materials. Volume 157(2017)
• Page Start: 382
• Page End: 391
• Publication Date: 2017-12-30
• Subjects: 3D printing -- Printability -- Buildability -- OPC-CSA blend -- Heat of hydration; Building materials -- Periodicals; 624.18
• DOI: 10.1016/j.conbuildmat.2017.09.109
• Languages: English
• ISSNs: 0950-0618

Abstract

Highlights: A printable OPC-CSA mix has been developed. Manual device has been used to simulate 3D printing. Mechanical properties of the printable mix has been studied. Abstract: Printing cementitious structures in 3D (3D Printing) requires the use of a mortar which setting is rigorously controlled. In this paper, a mix made out of two types of cement, ordinary Portland cement (OPC) and Calcium Sulfo-aluminate cement (CSA), was adopted to control the printability of a mortar. The latter was formulated in order to be extrudable, buildable and to reach a compressive strength comparable to that of a traditional mortar. Finally, a printable mix made out of 7% CSA and 93% OPC was developed. The cement paste of the developed mix was tested using isothermal calorimetry to study the impact of CSA on the heat of hydration of the mix. The mortar is first checked for the two characteristics of printability (extrudability and buildability) by a manual home-made device. Then, an estimation of the rheological properties of the mortar using a penetration test was done. Afterwards, the strength of the mortar was tested and a compressive strength of 88 MPa was found after 28 days for non-printed specimens and 79 MPa for printed specimens.