ADM guidance-ceramics: Fatigue principles and testing. Issue 11 (November 2017)

• Record Type: Journal Article
• Authors: Kelly, J.R.; Cesar, P.F.; Scherrer, S.S.; Della Bona, A.; van Noort, R.; Tholey, M.; Vichi, A.; Lohbauer, U.
• Is Part Of: Dental materials. Volume 33:Issue 11(2017)
• Page Start: 1192
• Page End: 1204
• Publication Date: 2017-11
• Subjects: Static fatigue -- Dynamic -- Cyclic loading -- Slow crack growth -- Ceramic fracture -- Degradation -- Lifetime -- SPT diagram -- S–N curve; Dentistry -- Periodicals; Dental materials -- Periodicals; 617.695
• DOI: 10.1016/j.dental.2017.09.006
• Languages: English
• ISSNs: 0109-5641

Abstract

Abstract: Background: Clinical failure of dental ceramics is usually reported as partial fracture of the restoration (chipping) or as catastrophic fracture of the whole structure. In contrast to metals, ceramics are linear-elastic, brittle materials exhibiting extremely low damage tolerance to failure. Well documented clinical and lab reports have shown this fracture event often occurs at loads far below their fracture strength due to intrinsic fatigue degradation via slow crack growth or cyclic fatigue mechanisms. The presence and development of surface flaws have a dominant role in damage accumulation and lifetime reduction of ceramic structures. Aims: This ADM guidance document aims to summarize the aspects related to fatigue degradation of dental ceramics, reviewing the concepts of fatigue testing and furthermore aims to provide practical guidance to young scientists entering into fatigue related research. The description of fatigue strength is always accompanied by a clear understanding of the underlying fracture mechanisms.