Anion-exchange synthesis of a nanoporous crystalline CoB2O4 nanowire array for high-performance water oxidation electrocatalysis in borate solution. Issue 34 (22nd August 2017)

• Record Type: Journal Article
• Authors: Zhu, Guilei; Yang, Lin; Zhang, Rong; Qu, Fengli; Liu, Zhiang; Du, Gu; Asiri, Abdullah M.; Yao, Yadong; Sun, Xuping
• Is Part Of: Nanoscale. Volume 9:Issue 34(2017)
• Page Start: 12343
• Page End: 12347
• Publication Date: 2017-08-22
• Subjects: Nanoscience -- Periodicals; Nanotechnology -- Periodicals; 620.505
• DOI: 10.1039/c7nr04344a
• Languages: English
• ISSNs: 2040-3364

Abstract

Abstract : A nanoporous crystalline CoB2 O4 nanowire array (CoB2 O4 /TM) behaves as a superior water oxidation catalyst electrode, requiring an overpotential of 446 mV to deliver 10 mA cm −2 in 0.1 M K-Bi (pH = 9.2). Abstract : Developing nanoporous nanoarray electrocatalysts for efficient water oxidation in environmentally benign media is highly desired but still remains a key challenge. In this communication, we report the fabrication of a nanoporous crystalline CoB2 O4 nanowire array on Ti mesh (CoB2 O4 /TM) from a Co(OH)F nanowire array on Ti mesh (Co(OH)F/TM) via an anion-exchange reaction. As a three dimensional (3D) catalyst electrode for water oxidation, CoB2 O4 /TM exhibits superior catalytic activity and needs an overpotential of only 446 mV to drive a geometrical catalytic current density of 10 mA cm −2 in 0.1 M potassium borate (pH = 9.2). Notably, this catalyst also shows strong long-term electrochemical durability with high turnover frequency values of 0.19 and 0.81 mol O2 per s at overpotentials of 400 and 500 mV, respectively.