Apatite formation on melt-derived bioactive glass powder based on SiO2-CaO-Na2O-P2O5 system. Issue 15 (15th October 2017)

• Record Type: Journal Article
• Authors: Ibrahim, Nurul Farhana; Mohamad, Hasmaliza; Mohd Noor, Siti Noor Fazliah; Ahmad, Nurazreena
• Is Part Of: Ceramics international. Volume 43:Issue 15(2017)
• Page Start: 11676
• Page End: 11685
• Publication Date: 2017-10-15
• Subjects: Melt-derived -- Quench -- Glass -- Tris-buffer -- Bioactivity; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2017.05.356
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: The higher melting temperature and longer soaking time during conventional glass melting route promoted the search for alternative in developing new bioactive glass (BG) composition with improved in fabrication temperature and melting time. The current project involved fabrication of new BG compositions based on SiO2 -CaO-Na2 O-P2 O5 system via melt derived route. It was confirmed that all bioactive glass composition can be melted at temperature lower than 1400 °C. Formation of Si-O-Si (tetrahedral) functional group highlighted that silicate based glass was established as detected by Fourier transform infrared spectroscope (FTIR). BG bioactivity was performed by incubating the BG powder in Tris-buffer solution (pH 8) for 7, 14 and 21 days. In vitro test confirmed the apatite formation on the bioactive glass surface upon soaking in Tris-buffer solution with characteristic of carbonate group (C-O) and P-O band noticed from FTIR and present of crystalline peak observed in X-ray diffraction (XRD). Morphology of apatite formation on BG surface was observed using scanning electron microscope (SEM).