Raman scattering from single WS2 nanotubes in stretched PVDF electrospun fibers. Issue 28 (6th July 2017)

• Record Type: Journal Article
• Authors: Grinberg, Olga; Deng, Shengwei; Zussman, Eyal; Livneh, Tsachi; Zak, Alla
• Is Part Of: Physical chemistry chemical physics. Volume 19:Issue 28(2017)
• Page Start: 18443
• Page End: 18451
• Publication Date: 2017-07-06
• Subjects: Chemistry, Physical and theoretical -- Periodicals; 541.3
• DOI: 10.1039/c7cp00934h
• Languages: English
• ISSNs: 1463-9076

Abstract

Abstract : Inorganic WS2 nanotubes (INT-WS2 ) were embedded into sub-μm polyvinylidene fluoride- co -hexafluropropylene (PVDF–HFP) electrospun fibers. Raman scattering was measured from single nanotubes during the stretching of individual nanocomposite fibers in order to elucidate their interactions with the polymer matrix. Abstract : Inorganic WS2 nanotubes (INT-WS2 ) were embedded into sub-μm polyvinylidene fluoride- co -hexafluropropylene (PVDF–HFP) electrospun fibers. In this report we explore the Raman scattering spectroscopy from a single nanotube during stretching of individual nanocomposite fibers. Red shifts of up to ∼4.7 cm −1 for A1g and E12g WS2 bands were found before reaching the "tearing point" of the fibers. These shifts may correlate with up to ∼2.8% of the WS2 nanotube elongation. Moreover, the absence of the A1g and E12g bands' broadening, as well as the nonappearance of the E22g shear mode in the nanotube Raman spectra, suggest the stretching of the nanotubes as a whole (including inner layers). These results point to the excellent adhesion of the nanotubes' surface to the polymer and to the effective load transfer from the polymer to the WS2 nanotube. In order to elucidate the nature of interaction between the polymer and the nanofiller, we modeled the deformation of composite fibers using an elastic lattice spring model (LSM). The results of the model are fully consistent with our interpretation.