Fatigue limit of monolithic Y-TZP three-unit-fixed dental prostheses: Effect of grinding at the gingival zone of the connector. (August 2017)

• Record Type: Journal Article
• Authors: Amaral, Marina; Villefort, Regina F.; Melo, Renata Marques; Pereira, Gabriel K.R.; Zhang, Yu; Valandro, Luiz Felipe; Bottino, Marco Antonio
• Is Part Of: Journal of the mechanical behavior of biomedical materials. Volume 72(2017)
• Page Start: 159
• Page End: 162
• Publication Date: 2017-08
• Subjects: Fixed prosthodontics -- Zirconium oxide partially stabilized by yttrium -- Grinding -- Fatigue; Biomedical materials -- Periodicals; Biomedical materials -- Mechanical properties -- Periodicals; Biomedical materials; Biomedical materials -- Mechanical properties; Periodicals; Electronic journals; 610.28
• DOI: 10.1016/j.jmbbm.2017.03.002
• Languages: English
• ISSNs: 1751-6161

Abstract

Abstract: Objectives: To determine the fatigue limits of three-unit monolithic zirconia fixed dental prosthesis (FDPs) before and after grinding of the gingival areas of connectors with diamond burs. Material and methods: FDPs were milled from pre-sintered blocks of zirconia simulating the absence of the first mandibular molar. Half of the specimens were subjected to grinding, simulating clinical adjustment, and all of them were subjected to glazing procedure. Additional specimens were manufactured for roughness analysis. FDPs were adhesively cemented onto glass-fiber reinforced epoxy resin abutments. Fatigue limits and standard deviations were obtained using a staircase fatigue method (n=20, 100, 000 loading cycles/5 Hz). The initial test load was 70% of the mean load-to-fracture (n=3) and load increments were 5% of the initial test load for both the control and ground specimens. Data were compared by Student's T -test (α≤0.05). Results: Both the control and ground groups exhibited similar values of load-to-fracture and fatigue limits. Neither the surface treatments nor ageing affected the surface roughness of the specimens. Conclusions: The damage induced by grinding with fine-grit diamond bur in the gingival area of the connectors did not decrease the fatigue limit of the three-unit monolithic zirconia FDP.