Grain-size dependence of the deterioration of oxygen transport for pure and 3 mol% Zr-doped Ba0.5Sr0.5Co0.8Fe0.2O3−δ induced by thermal annealing. Issue 10 (16th February 2017)

• Record Type: Journal Article
• Authors: Saher, Saim; Meffert, Matthias; Störmer, Heike; Gerthsen, Dagmar; Bouwmeester, Henny J. M.
• Is Part Of: Journal of materials chemistry. Volume 5:Issue 10(2017)
• Page Start: 4982
• Page End: 4990
• Publication Date: 2017-02-16
• Subjects: Materials -- Research -- Periodicals; Chemistry, Analytic -- Periodicals; Environmental sciences -- Research -- Periodicals; 543.0284
• DOI: 10.1039/c6ta10454a
• Languages: English
• ISSNs: 2050-7488

Abstract

Abstract : Grain size, temperature and Zr-substitution are found to influence the performance decay of the mixed-conducting perovskite oxide Ba0.5 Sr0.5 Co0.8 Fe0.2 O3− δ . Abstract : In this study, the influence of long-term annealing at intermediate temperatures on oxygen transport of Ba0.5 Sr0.5 Co0.8 Fe0.2 O3− δ (BSCF) and 3 mol% Zr-doped BSCF (BSCF-Z3) ceramics with different grain sizes was studied by means of in situ electrical conductivity relaxation (ECR) measurements. Ceramics with different grain sizes in the range of 3–80 μm were obtained by varying the temperature and dwell time during sintering. For both compositions, the apparent values of the chemical diffusion coefficient D chem and surface exchange coefficient k chem extracted from the data of ECR measurements are found to decrease with the time of annealing. The strongly correlated decreases in D chem and k chem, being greater in magnitude at a lower grain size and temperature, are observed significantly more pronounced for BSCF than for BSCF-Z3. The results from microstructural analysis provide a clear rationale for the observations from ECR. High-resolution transmission electron microscopy (TEM) images recorded before and after annealing under pure oxygen at 700 °C for 13 d show excessive formation of hexagonal and plate-like lamellar precipitates at the grain boundaries and in the interior of grains of BSCF ceramics during the annealing process, whilst secondary phase formation is restricted solely to the grain boundary regions in BSCF-Z3. The possible importance of grain boundaries in determining the oxygen surface exchange kinetics is emphasized.