Dielectric properties of Sr0.5Ca0.5TiO3: x Pr3+ ceramics. Issue 8 (1st June 2017)

• Record Type: Journal Article
• Authors: Vidyadharan, Viji; Sreeja, E.; Kumar A, Santhosh; Joseph, Cyriac; Unnikrishnan, N.V.; Biju, P.R.
• Is Part Of: Ceramics international. Volume 43:Issue 8(2017)
• Page Start: 6268
• Page End: 6275
• Publication Date: 2017-06-01
• Subjects: Sr0.5Ca0.5TiO3 -- Dielectric properties -- Conductivity -- Power-law parameters -- Cole-Cole plot; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2017.02.031
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: The frequency dependent dielectric and AC conductivity properties of different concentrations of Pr 3+ doped Sr0.5 Ca0.5 TiO3 ceramics were investigated for the frequency range 100 Hz to 2 MHz at different temperatures. The morphology of the prepared samples was analyzed by using Field-Emission Scanning Electron Microscope images. The value of dielectric constant and dielectric loss decreases with increase in the frequency of the applied signal in all the samples. Also, the value of dielectric constant and dielectric loss decreased with doping of different concentrations of Pr 3+ ions. The conductivity of the samples obeys Jonscher's power-law and shows a decrease with increasing doping concentration of Pr 3+ ions. The higher value of real and imaginary part of impedance at lower frequency indicates the space charge polarization of the material and its absence at higher frequencies was confirmed from the low value of impedance at higher frequency region. The Cole- Cole parameters of the samples were calculated and the semi-circle observed indicates a single relaxation process and can be modeled by an equivalent parallel RC circuit. At lower frequency region, the value of dielectric constant and dissipation factor increases with increase in the temperature. Also the value of conductivity increases with temperature at high frequency region, due to the enhanced mobility of charge carriers.