In-situ electrochemical impedance spectroscopy measurements of zirconium alloy oxide conductivity: Relationship to hydrogen pickup. (1st May 2017)

• Record Type: Journal Article
• Authors: Couet, Adrien; Motta, Arthur T.; Ambard, Antoine; Livigni, Didier
• Is Part Of: Corrosion science. Volume 119(2017)
• Page Start: 1
• Page End: 13
• Publication Date: 2017-05-01
• Subjects: Hydrogen pickup -- Fuel cladding corrosion -- EIS -- Oxide resistivity; Corrosion and anti-corrosives -- Periodicals; 620.11223
• DOI: 10.1016/j.corsci.2016.12.008
• Languages: English
• ISSNs: 0010-938X

Abstract

Highlights: In-situ electrochemistry on zirconium alloys in 360 °C pure water show oxide layer resistivity changes during corrosion. A linear relationship is observed between oxide resistivity and instantaneous hydrogen pickup fraction. The resistivity of the oxide layer formed on Zircaloy-4 (and thus its hydrogen pickup fraction) is higher than on Zr-2.5Nb. Abstract: Hydrogen pickup during nuclear fuel cladding corrosion is a critical life-limiting degradation mechanism for nuclear fuel. Following a program dedicated to zirconium alloys, corrosion, it has been hypothesized that oxide electronic resistivity determines hydrogen pickup. In-situ electrochemical impedance spectroscopy experiments were performed on Zircaloy-4 and Zr-2.5Nb alloys in 360 °C water. The oxide resistivity was measured as function of time. The results show that as the oxide resistivity increases so does the hydrogen pickup fraction. The resistivity of the oxide layer formed on Zircaloy-4 is higher than on Zr-2.5Nb, resulting in a higher hydrogen pickup fraction of Zircaloy-4, compared to Zr-2.5Nb.