Nanomechanical properties of gas-borided layer produced on Nimonic 80A-alloy. Issue 11 (1st August 2017) - Makuch, Natalia
Abstract: Diffusion borided layers, fabricated on Ni-based alloys, were characterized by improved hardness and wear resistance. In this paper, gas boronizing in N2 –H2 –BCl3 atmosphere was proposed to produce the ceramic phases (borides) on Nimonic 80A-alloy. This process was carried out at 920 °C (1193 K) for 2 h. The microstructure was studied in detail using scanning electron microscope and energy-dispersive X-ray microanalysis. The boride layer consisted of a mixture of nickel borides (Ni3 B, Ni2 B, Ni4 B3, NiB) and chromium borides (CrB, Cr2 B). The nanomechanical properties (Young's modulus and hardness) were examined using the nanoindenter with a Berkovich diamond tip. The load-displacement curves and the indentation images were shown for the selected measurements. The identified phases in microstructure were very fine, therefore it was impossible to measure the hardness and Young's modulus of a defined phase. However, the percentage of chromium and nickel borides' mixtures was calculated based on the measurements of indentation hardness ( H IT ) compared to the previous work. It enabled to calculate Poisson's ratio for a specified indentation. As a consequence, the indentation moduli E IT were determined. The higher values of H IT and E IT were obtained in case of indents, performed in the areas of higher percentage of chromium borides.