Effect of laser treatment parameters on surface modification and tribological behavior of AISI 8620 steel. (August 2017)

• Record Type: Journal Article
• Authors: Roy, Sougata; Zhao, Jingnan; Shrotriya, Pranav; Sundararajan, Sriram
• Is Part Of: Tribology international. Volume 112(2017)
• Page Start: 94
• Page End: 102
• Publication Date: 2017-08
• Subjects: Steel -- Laser heat treatment -- Surface modification -- Wear resistance; Tribology -- Periodicals; 621.89
• DOI: 10.1016/j.triboint.2017.03.036
• Languages: English
• ISSNs: 0301-679X

Abstract

Abstract: In this study, the effect of different shielding gas and laser scanning velocity on the resulting retained austenite (RA) content and tribomechanical properties of AISI 8620 steel were investigated. RA generation was comparatively lower at higher scanning velocity and with argon as the shielding gas due to lower beam interaction time and inert environment. Varied heat input and differing reaction volume resulted in different hardness levels on these samples. Air shielded samples showed slightly higher friction coefficient than the other samples due to higher surface roughness and shearing of oxide layers. The nitrogen shielded samples exhibited the best wear resistance among all samples, which was attributed to nitride formation on surface and to high hardness resulting from the laser treatment. Highlights: Laser treatment of AISI 8620 steel results in phase transformation based hardening. Tuning laser power density and scanning velocity can control RA below 10%. Argon as a shielding gas generates lower RA% compared to air and nitrogen.