Cavitation erosion of plasma sprayed YSZ coatings produced by feedstocks with different initial sizes. (July 2017)

• Record Type: Journal Article
• Authors: Wang, Yan; Darut, Geoffrey; Poirier, Thierry; Stella, Jorge; Liao, Hanlin; Planche, Marie-Pierre
• Is Part Of: Tribology international. Volume 111(2017)
• Page Start: 226
• Page End: 233
• Publication Date: 2017-07
• Subjects: YSZ -- Cavitation erosion -- Surface degradation -- Size distribution of pore; Tribology -- Periodicals; 621.89
• DOI: 10.1016/j.triboint.2017.03.019
• Languages: English
• ISSNs: 0301-679X

Abstract

Abstract: Cavitation erosion of plasma sprayed yttria stabilized zirconia coatings produced by feedstocks with different initial sizes was investigated according to the main guidance of ASTM-G32. Prior to thermal spray, substrates were preheated to 150 and 300 °C. The size distribution of pores on the surface of coatings (as-sprayed and eroded) was estimated specifically to investigate its influences on the surface degradation during cavitation erosion. The results indicate that high feedstock size leads to high porosity of coating and low microhardness along with low resistance against cavitation erosion. Additionally, preheating processes could improve the coating resistance against cavitation erosion. The pore size distribution analysis results reveal that initial pores grow up and coalesce and cavitation pits format during cavitation erosion tests. Highlights: YSZ coatings were manufactured by APS with different particles sizes and substrate preheating processes. Cavitation erosion resistance of YSZ coatings were investigated. Cavitation damage is a surface degradation process with initial pores growing and cavitation pits formatting. Bubble collapsing could induce shear stress to the solid wall of pores.