Crystal structure and near-infrared reflective properties of Fe3+ doped AlPO4 pigments. Issue 8 (1st June 2017)

• Record Type: Journal Article
• Authors: Shi, Yong; Zhong, Mingfeng; Zhang, Zhijie; Wang, Da
• Is Part Of: Ceramics international. Volume 43:Issue 8(2017)
• Page Start: 5979
• Page End: 5983
• Publication Date: 2017-06-01
• Subjects: Coprecipitation process -- Inorganic pigments -- Near-infrared reflectance -- Cool colorants; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2017.01.131
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Novel non-toxic orange yellow inorganic pigments Al1−x Fex PO4 (x=0.00, 0.03, 0.05, 0.08) with high near-infrared reflectance (NIR) have been synthesized by a coprecipitation method. The structures of samples were investigated by XRD and Raman spectroscopy, and the reflective properties were tested by UV–vis–NIR spectrophotometer. Results demonstrated that with more Fe 3+ added, the color of the powder samples changed from white to orange yellow and the near-infrared reflectance decreased from 98.03% to 72.56%, which is higher than the commercial orange yellow pigment (61.99%). The near-infrared reflectance of corresponding coatings decreased from 69.35% to 59.10%, which is higher than the commercial coating with the similar color (51.88%). From the XRD diffraction spectrogram, we can see the peaks did not change with more Fe 3+ added. However, because of ionic radius of Fe 3+ (0.63 Å) is a little larger than Al 3+ (0.53 Å), the cell volume increases a little when more Fe 3+ is added. Furthermore, from the Raman spectrogram, we can see that doping with Fe 3+, there is a new Raman peak which is assigned to the asymmetric [FeO4 ] stretch. In addition, replacing Fe 3+ for Al 3+ in AlPO4 caused the band gap decreased from 5.98eV to 3.60 eV, which can cause the absorption of more near-infrared radiation and that is the reason of the decrease of near-infrared reflectance.