Oriented attachment of ultra-small Mn(1−x)ZnxFe2O4 nanoparticles during the non-aqueous sol–gel synthesis. Issue 12 (18th December 2014)

• Record Type: Journal Article
• Authors: Masthoff, I.-C.; Gutsche, A.; Nirschl, H.; Garnweitner, G.
• Is Part Of: CrystEngComm. Volume 17:Issue 12(2015)
• Page Start: 2464
• Page End: 2470
• Publication Date: 2014-12-18
• Subjects: Crystals -- Periodicals; Crystal growth -- Periodicals; Crystallography -- Periodicals; Cristaux -- Périodiques; Cristaux -- Croissance -- Périodiques; Cristallographie -- Périodiques; 548
• DOI: 10.1039/c4ce02068e
• Languages: English
• ISSNs: 1466-8033

Abstract

Abstract : We show that clustered magnetic Mn(1− x ) Zn x Fe2 O4 nanocrystals with shamrock-type shape form through oriented attachment during the non-aqueous sol–gel synthesis. The Curie temperature of these nanocrystals can be tuned by modification of the Mn/Zn ratio. Abstract : The advantages of ultra-small manganese–zinc ferrite nanoparticles are manifold and can be exploited in a wide range of applications. Here we show that ultra-small, highly crystalline Mn–Zn ferrite nanoparticles with variable compositions can be obtained by non-aqueous sol–gel synthesis in a facile, scalable process. The growth of Mn0.6 Zn0.4 Fe2 O4 nanoparticles has been investigated exemplarily for a series of Mn–Zn ferrites. It is thereby shown that the initially formed ultra-small 2 nm sized particles grow via oriented attachment into shamrock-like shaped particles, and clusters with an ordered structure are formed during synthesis. Throughout the synthesis, the crystallinity of the particles improves until after 24 h of synthesis highly crystalline, monodisperse nanostructures with a size of around 6 nm are obtained. Furthermore, the influence of the chemical as well as physical properties of the ultra-small Mn(1− x ) Zn x Fe2 O4 nanoparticles with 0 ≤ x ≤ 1 on their Curie temperature was evaluated. It is shown that by variation of the Mn/Zn ratio the Curie temperature of the particles can be tailored in a broad range from 200 to 400 °C.