Comparison of cellulose and chitin nanocrystals for reinforcing regenerated cellulose fibers. Issue 22 (31st January 2017)

• Record Type: Journal Article
• Authors: Chen, Jing‐Huan; Liu, Jin‐Gang; Yuan, Tong‐Qi; Sun, Run‐Cang
• Is Part Of: Journal of applied polymer science. Volume 134:Issue 22(2017)
• Page Start: n/a
• Page End: n/a
• Publication Date: 2017-01-31
• Subjects: cellulose -- cellulose nanocrystals -- chitin nanocrystals -- regenerated fiber -- reinforcement; Polymers -- Periodicals; Polymerization -- Periodicals; 668.9
• DOI: 10.1002/app.44880
• Languages: English
• ISSNs: 0021-8995

Abstract

ABSTRACT: In this study, regenerated cellulose fibers reinforced by cellulose nanocrystals (CENC) and chitin nanocrystals (CHNC) were prepared by blending the nanocrystals suspensions with the cellulose solution in NaOH/urea/water solvent at room temperature. The effect of nanocrystals' addition on the properties of spinning dopes and regenerated fibers were investigated and compared. Results showed that the obtained CENC and CHNC had different dimensions, and both of them increased the viscosity and decreased the transparency of the spinning dopes. However, the dissolution state of cellulose was not changed. CHNC had a greater influence on the properties of spinning dopes, while CENC had more obvious effect on the performance of regenerated fibers. The CENC reinforced fibers showed a higher crystallinity index as compared to the CHNC reinforced fibers. The tensile strength of the regenerated fibers was evidently improved when 3 wt % CENC or 2 wt % CHNC were added, while the elongation at break of the fibers was slightly decreased with the increase of nanocrystals content. The morphology and thermal stability of the regenerated fibers was not affected by the addition of nanocrystals. This study suggested that the dimension, group and content of nanocrystals were important factors for the reinforcement of regenerated cellulose fibers. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci.2017, 134, 44880. Abstract :