Effect of UV irradiation on magnetic behavior of reduced graphene oxide decorated with nickel nanostructure. Issue 6 (15th April 2017)

• Record Type: Journal Article
• Authors: Sharma, Geeta; Gosavi, S.W.
• Is Part Of: Ceramics international. Volume 43:Issue 6(2017)
• Page Start: 4888
• Page End: 4894
• Publication Date: 2017-04-15
• Subjects: Graphene -- Composite -- Magnetism -- UV-irradiation; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2016.12.137
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: Reduced graphene oxide (RGO) decorated with nickel has been synthesized via an in-situ reduction of graphene oxide (GO) and nickel nitrate using NaOH and hydrazine. The starting materials Ni (NO3 )2 and GO were taken in two different ratios and the products formed were designated as RGNi2 and RGNi1 . The formation of the composite was confirmed by the appearance of X-ray diffraction peaks at 44.5°, 51.9°, 76.5° corresponding to Ni and at 24.8°and 43.2° for RGO. The RGNi2 was irradiated with UV light (λ=254 nm) for different durations (2, 6, 12, 24 and 48 h). Intensity ratio of d and g-bands (Id /Ig ) of Raman spectra increases from 1.18 to 1.47 over the duration of irradiation period (2–48 h). The magnetization measurements using the vibrating sample magnetometer (VSM) of these samples reveal their ferromagnetic behavior. The calculated saturation magnetization (MS ) value of Ni, RGNi1 and RGNi2 is 47.86, 30.56 and 8.25 emu/g respectively and the corresponding coercivity (HC ) value is found to be 181, 227 and 296 Oe. The MS of RGNi2 is found to increase to 10.65 emu/g after 48 h of irradiation. This enhancement in the MS (~23%) with irradiation may be due to defect formation by the UV light.