Simple and effective failure analysis of dissimilar resistance spot welded advanced high strength steel sheets. (February 2017)

• Record Type: Journal Article
• Authors: Noh, Wooram; Kim, Wonjae; Yang, Xin; Kang, Moonjin; Lee, Myoung-Gyu; Chung, Kwansoo
• Is Part Of: International journal of mechanical sciences. Volume 121(2017)
• Page Start: 76
• Page End: 89
• Publication Date: 2017-02
• Subjects: Advanced high strength steels -- Dissimilar weld -- Failure analysis -- Mechanical properties of weld -- Numerical inverse approach; Mechanical engineering -- Periodicals; Génie mécanique -- Périodiques; Mechanical engineering; Maschinenbau; Mechanik; Zeitschrift; Periodicals; 621.05
• DOI: 10.1016/j.ijmecsci.2016.12.006
• Languages: English
• ISSNs: 0020-7403

Abstract

Abstract: The failure of welded structures was analyzed considering dissimilar combinations of advanced high strength steels (AHSS) and a conventional mild steel. A method to characterize the mechanical properties of hardening behavior along with the deterioration associated with micro-void development and fracture criterion based on a modified damage model was applied by employing simple but effective experimental and numerical inverse procedure. The proposed procedure was solely based on standard and miniature simple tension tests for base sheets and weld nuggets, respectively. The identified plastic and failure properties were applied to the analysis of the failure mode and strength in the two well-accepted coupon tests of lap-shear and U-shape tension tests for DP980-TRIP980 and GMW2-TRIP980 dissimilar welded sheets. The analysis confirmed that the distinct failure behavior in the coupon tests for the two dissimilar weld cases was mainly due to the competition between the element with high strength/low ductility and the element with low strength/high ductility. Highlights: Failure behavior of dissimilar welded structures for AHSS sheets was analyzed. A simple but effective property characterization method in dissimilar welded structure was developed. Mechanical properties of weld nuggets were analyzed in macro and micro scale levels. The cause of distinct failure behavior in the coupon tests for dissimilar welds was analyzed.