Heat treatment effect on wear behaviour of HVOF-sprayed near-nanostructured coatings. (2nd January 2017)

• Record Type: Journal Article
• Authors: Ben Mahmud, T.; Khan, T. I.; Farrokhzad, M. A.
• Is Part Of: Surface engineering. Volume 33:Number 1(2017)
• Page Start: 72
• Page End: 82
• Publication Date: 2017-01-02
• Subjects: Nanostructure -- Coatings -- HVOF spraying -- Heat treatment -- Abrasive wear; Surfaces (Technology) -- Periodicals; Coatings -- Periodicals; 620.4405
• DOI: 10.1080/02670844.2016.1258769
• Languages: English
• ISSNs: 0267-0844

Abstract

Abstract : This study investigates the effect of heat treatment on changes in microstructure and wear behaviour of WC-NiCr coatings. Two feedstock powders with a similar chemical composition and different particle sizes (near nano-structured WC-17NiCr and microstructured WC-15NiCr) were used. High-velocity oxyfuel spraying technique was used to deposit coatings on to a mild steel substrate using identical spraying parameters. Coated samples were then heat treated in a nitrogen atmosphere at 500 and 700°C. The effect of heat treatment on changes in hardness and wear performance of the coatings was studied using microstructural analysis, micro-hardness indentation and abrasive wear tests. The results showed that the heat treatment increased the hardness of both coatings and a corresponding increase in wear resistance was recorded. The formation of a brittle CrWO4 phase in the microstructured coating resulted in brittle fracture of the coating and this gave lower wear resistance compared to the nanostructured coatings.